Hernon Tuffbond 394 Technical Data Sheet |
您所在的位置:网站首页 › HERNON胶水302 › Hernon Tuffbond 394 Technical Data Sheet |
Product Description Hernon Tuffbond 394 is a single component, high temperature resistant, heat activated epoxy. It cures to a high performance thermoset system with excellent adhesion properties to a wide variety of substrates. The rapid curing mechanism of 1.5 minutes at a bondline temperature of 150ºC makes it ideal for production line use. Tuffbond 394 will change from amber-yellow to a reddish brown upon cure.
Bonding the voice coil to the cone has been a challenge for engineers, specifically when the adhesive temperature resistance requirement is above 200ºF (93ºC). Two component epoxy has been most commonly used for this application, but limitations such as mixing ratio, cure speed, potential solidification in equipment and static mixers and the need for equipment flushing solvents have made Tuffbond 394 more practical.
Product Benefits • High temperature resistance. • Single component (no mixing, no pot life). • Solventless. • Cures on demand (heat cure). • Will not slip during cure. • Fast setting: 1.5 minutes at 150oC bondline. • Changes color upon cure (yellow to brown). • Excellent adhesion to various substrates. • Gives high shear. • Low water absorption. • Very rigid. • Low density. • No porosity upon cure.
Typical Properties (Uncured) Property Value Resin Epoxy Appearance Amber-yellow liquid Viscosity @ 25ºC, cP 44,000 to 56,000 Specific gravity 1.19 Flash point See MSDS
Curing Characteristics Tuffbond 394 can be cured by infra-red or convection oven. Cure time will depend on the bondline temperature. Temperature, ºC (ºF) Cure Time, minutes 150 (300) 0.5 120 (250) 1 100 (212) 6 Typical Properties (Cured) Property Value Heat Resistance, ºC (ºF) 204 (400) Elongation, % 6.1 Typical Cured Performance Shear Strength, ISO 4587 Cured 5 minutes at 150ºC Substrate Shear Strength, N/mm² (psi) Steel 13.8 (2000) Aluminum 12.4 (1800) Typical Environmental Resistance Chemical/Solvent Resistance Shear Strength, gritblasted steel, ISO 4587 Cured 2 minutes at 150ºC 30 days immersion in chemical/solvent Chemical/Solvent % Initial Strength Retained Water 100 Sulfuric Acid 99 Ammonia, 25% 99 Methanol 97 Xylene 98
General Information This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials. For safe handling information on this product, consult the Material Safety Data Sheet (MSDS).
Storage Tuffbond 394 must be stored under refrigeration at a temperature of 35 to 40ºF for extended shelf life. To prevent contamination of unused material, do not return any material to its original container.
Dispensing Equipment Hernon offers a complete line of semi and fully automated dispensing equipment. Contact Hernon Sales for additional information. 点击下载附件查看之:
|