干粉激发煤矸石基地质聚合物性能影响因素研究

张大明

;

任凤玉

【摘

要】

For activating coal gangue in a more efficient and safer way to 

produce the qualified geopolymer for construc-tion,alkaline dry powder 

activator made of sodium hydroxide and calcium carbonate powder is 

used to replace hydroxide solu-tion to treat coal gangue,fly ash and sand. 

Factors affecting the characteristics of the geopolymer of coal gangue 

activated by al-kaline dry powder were studied,which is contrasted with 

that of the traditional sodium hydroxide solution. The results showed 

that:①Elevating curing temperature and increasing the dosage of sodium 

hydroxide in dry powder accelerated the setting and hardening of the 

geopolymer.②Elevating curing temperature increased water absorption 

and compressive strength of the speci-

men.③The increase of calcium 

carbonate in dry powder raised water absorption rate and compressive 

strength of geopolymer specimen.④When sodium hydroxide amount in 

dry powder reached 3%, geopolymer specimen with lowest water 

absorption rate and highes

t compressive strength was obtained.⑤Whether 

from the viewpoints of water absorption rate or compressive strength,the 

effect of dry powder activator outperforms that of sodium hydroxide 

solution activator. Thus,dry powder activator is more suitable for preparing 

coal gangue-based geopolymer than sodium hydroxide solution activator.%

为更方便、高效、安全地激发煤矸石的活性

,

制造出满足建筑需要的地质聚合物

,

用

氢氧化钠与碳酸钙混合制备的碱性干粉激发剂替代氢氧化钠

,

对煤矸石、粉煤灰和